Saleh, B. (2013). SLURRY EROSION-CORROSION RESISTANCE OF ELECTROLESS Ni-P PLATING ON AISI 5117 STEEL. JES. Journal of Engineering Sciences, 41(No 4), 1467-1479. doi: 10.21608/jesaun.2013.114869
B. Yosseif Mohamed Saleh. "SLURRY EROSION-CORROSION RESISTANCE OF ELECTROLESS Ni-P PLATING ON AISI 5117 STEEL". JES. Journal of Engineering Sciences, 41, No 4, 2013, 1467-1479. doi: 10.21608/jesaun.2013.114869
Saleh, B. (2013). 'SLURRY EROSION-CORROSION RESISTANCE OF ELECTROLESS Ni-P PLATING ON AISI 5117 STEEL', JES. Journal of Engineering Sciences, 41(No 4), pp. 1467-1479. doi: 10.21608/jesaun.2013.114869
Saleh, B. SLURRY EROSION-CORROSION RESISTANCE OF ELECTROLESS Ni-P PLATING ON AISI 5117 STEEL. JES. Journal of Engineering Sciences, 2013; 41(No 4): 1467-1479. doi: 10.21608/jesaun.2013.114869
SLURRY EROSION-CORROSION RESISTANCE OF ELECTROLESS Ni-P PLATING ON AISI 5117 STEEL
Mechanical Eng Department, Faculty of Engineering, Assiut University, Assiut, Egypt
Abstract
In this research, slurry erosion-corrosion and slurry-erosion resistances of electroless Ni-P coatings have been investigated. These coatings were applied on AISI 5117 steel discs by electroless deposition process and then they were heat treated at 650 C for 1 h. Slurry erosion-corrosion and slurry-erosion resistances of deposits were measured by the whirling-arm tester. Also, microstructure of deposits before and after heat treatment was evaluated by X-ray diffraction (XRD) analysis. The results showed that the electroless Ni-P plating greatly increased the erosion and erosion-corrosion resistances for all impact angles. Moreover, the effectiveness of plating was the highest for an impact angle of 45o, where the erosion and erosion-corrosion resistances were increased by 60% and 70% respectively, compared with that of the substrate. The results showed also that the coated and blank specimens behaved as ductile materials under erosion and erosion-corrosion tests and the maximum weight loss occurred at an impact angle of 45o.